Technical data sheets
Compare 30 µm and 50 µm NanoPaper, review measured properties and download the technical data sheets.
Compare material properties
Reference values from the current technical data sheets.
| Property | 30 µm | 50 µm |
|---|---|---|
| Nominal thickness | 30 µm | 50 µm |
| Sheet dimensions | 297 × 210 mm (A4) | 297 × 210 mm (A4) |
| Basis weight | 30–35 g/m² | 50–55 g/m² |
| Tensile strength | 62.1 ± 13.4 MPa | 61.8 ± 5.0 MPa |
| Elastic modulus | 1.8 ± 0.2 GPa | 1.7 ± 0.4 GPa |
| Elongation | 5.7 ± 1.8% | 6.8 ± 1.2% |
Mechanical values are mean ± standard deviation; seven specimens per grade. Test conditions are given in each PDF.
Surface roughness
Ra measured at 50× magnification. Values are mean ± standard deviation.
| Surface | 30 µm · Ra (µm) | 50 µm · Ra (µm) |
|---|---|---|
| Side A | 1.24 ± 0.28 · 7 profiles | 2.23 ± 0.35 · 7 profiles |
| Side B | 1.10 ± 0.41 · 7 profiles | 2.11 ± 0.32 · 8 profiles |
See each TDS for the equipment, settings and Sa values.
Processing examples
Silver inks
150 °C for 30 minutes
Copper ink
TLC 5500T setting 200 °C
Six passes; estimated cumulative residence time ≈30 s.
These examples describe selected ink systems.